MGB-A90A
Data Sheet
This high performance PTMEG polyether system is one of a family of polymer systems developed by Northstar Polymers for demanding work environments. Urethane elastomers molded with this system exhibit high rebound or “High Energy”. The high rebound combined with its low coefficient of friction, yields elastomers with outstanding abrasion resistance. They also meet the requirements of 21 CFR 177.1680, FDA direct dry food contact. This combination of features makes elastomers molded from MGB-A90A perfect for many applications including the handling of mined materials, wood chips, grain, gravel, sand, and other very fine particle-size, sliding commodities, and many custom applications. This product is recommended for long-term use in constant aqueous environments.
Typical Physical Properties
Physical Property
ASTM #
Typical Value
Durometer Hardness:
D 2240
Shore A 90
Modulus (psi):
100% Elongation:
D 412
1460
Tensile Strength (psi):
D 412
3610
Ultimate Elongation (%):
D 412
840
Tear Resistance (pli)
Die C:
D 624
560
Split:
D 624
134
Taber Abrasion (mg loss):
D 4060
35
Bashore Rebound (%):
D 2632
62
Typical Processing Conditions
Prepolymer:
MGA-048
Curing Agent:
BNA-005
Catalyst Type:
Amine
Catalyst Level:
Included
Prepolymer Temperature (ºF):
180 - 200
Curing Agent Temperature (ºF):
77
Mold Temperature (ºF):
180 -200
Pot Life*(minutes):
2.5 - 3.0
De-mold Time*** 200 °F (minutes):
25 - 35
Complete Cure Cycle*** 180 °F (hours):
16
* Defined as: a 300 gram sample is too thick to pour.
** Defined as: no string of urethane develops when touched.
*** The use of catalyst will increase the rate of cure, but will decrease Pot Life.
Typical Mixing Ratio
Prepolymer (A) Curing Agent (B)
Code Number: MGA-048 BNA-005
Specific Gravity: 1.070 1.017
Equivalent Weight: 483 45
Stoichiometry: 1.00 0.95
NCO/OH Index: 1.05 1.00
Weight Pph: 91.9 8.1
Weight Ratio: 1.000 0.089
Weight Ratio: 11.298 1.000
Volume Pph: 91.5 8.5
Volume Ratio: 1.000 0.093
Volume Ratio: 10.736 1.000
The actual mixing ratio at the operation may need to be adjusted based on the actual stoichiometric ratio calculation. For machine mixing, calibration of the metering system is recommended before the new batch of raw material is used.
Northstar Polymers, LLC
3444 Dight Avenue South
Minneapolis, MN 55406
Tel: 612.721.2911
Fax: 612.721.1009
E-Mail: info@northstarpolymers.com
Notice: All of the statements, recommendations, suggestions, and data concerning the subject material are based on our laboratory results, and although we believe the same to be reliable, we expressly do not represent, warrant, or guarantee the accuracy, completeness, or reliability of same, or the material or the results to be obtained from the use thereof, neither do we warrant that any such use, either alone or in combination with other materials, shall be free of the rightful claim of any third party by way of INFRINGEMENT or the like, and NORTHSTAR POLYMERS DISCLAIMS ALL WARRANTIES, EXPRESS OR IMPLIED, OF MERCHANTABILITY and FITNESS FOR A PARTICULAR PURPOSE.